Our products

Products:
Alkyd automotive enamel
Thinner for alkyd enamel
Substrates:
Sanded factory coating
Primed and filled surfaces
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding.
Prime the surface with an anticorrosion primer.
Perform dry sanding with P320-P400 or wet sanding with P800-P1000.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Thinning:
Thinner, up to 35% of the enamel mass.
Application Viscosity:
18-20 seconds at 20°C using B3-4 (DIN Cup 4).
Application Equipment:
Compliant spray gun:
Nozzle size: 1.2 - 1.5 mm
Working pressure: 3.0 - 5.0 atm
HVLP spray gun:
Nozzle size: 1.4 - 1.8 mm
Working pressure: 2.5 - 3.0 atm
Flash-off time: 5-7 minutes between layers.
Coating Thickness: 35-40 microns for 2 layers.
Number of Layers: 2-3
Drying:
At 20°C: 8 hours
At 60°C: 1 hour
Equipment Cleaning: Solvent 646/647
Shelf Life: 24 months.

A two-component acrylic clearcoat.
Products:
2K acrylic clearcoat 2+1 MS
Hardener for 2+1 MS clearcoat
Vikron acrylic thinner
Substrates:
Sanded factory coating
Primed and filled surfaces
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P240-P320.
Prime the surface sanded down to metal with WASH PRIMER VL-02 anticorrosion primer.
Apply 2K acrylic primer (3+1, 4+1, or 5+1), then dry sand with P320-P400 or wet sand with P800-P1000.
Apply metallic base coat.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Mixing:
Clearcoat: hardener = 2:1
Pot Life: 1.5 hours at 20°C
Application Equipment:
Compliant spray gun:
Nozzle size: 1.4 - 1.6 mm
Working pressure: 2.0 atm
HVLP spray gun:
Nozzle size: 1.3 - 1.7 mm
Working pressure: 2.0 atm
Flash-off time: 10 minutes
Coating Thickness: 35-45 microns / 2 layers
Number of Layers: 2.5-3
Drying:
At 20°C — 12 hours
At 60°C — 60 minutes
At 80°C — 30 minutes
Equipment Cleaning:
Metallic thinner
Solvent 646/647
Shelf Life: 24 months.

A single-component primer designed for plastic parts, intended for the initial priming of plastic surfaces and enhancing adhesion of paint coatings. Suitable for use on plastic components, including polypropylene, without the need for flame treatment.

Color: Transparent, metallic
Substrates:
Most plastics used in the automotive industry.
Note: Vikron 1K cannot be applied to certain types of plastics (e.g., PE).
Not suitable for plastics sensitive to organic solvents, such as polystyrene (PS).
Surface Preparation:
Use a plastic cleaner to clean the surface.
Use tack cloths to remove dust.
Application Equipment:
Compliant spray gun:
Nozzle size: 1.4 - 1.6 mm
Working pressure: 2.8 - 3.1 atm
HVLP spray gun:
Nozzle size: 1.3 - 1.7 mm
Working pressure: 2.0 atm
Mixing: Ready to use.
Number of Layers: 1 full layer.
Flash-off Time: 10 minutes at 20°C.
Drying: 10 minutes at 20°C.
Next Coating: Basecoats and acrylic enamels can be applied over the Vikron 1K plastic primer.
Shelf Life: 24 months.

Developed for Use in the Automotive Glass Replacement Segment It provides excellent adhesion to major structural materials such as glass, painted metals, aluminum, plastics, wood, and more.

Designed for Seam Sealing and Bonding

It is intended for seam sealing, bonding non-load-bearing elements, as well as reducing vibration and improving sound insulation properties during vehicle repair and manufacturing.

A two-component acrylic clearcoat.

Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P240-P320.
Prime the surface that has been sanded down to the metal using WASH PRIMER VL-02 anticorrosion primer.
Apply 2K acrylic primer (3+1, 4+1, or 5+1), followed by dry sanding with P320-P400 or wet sanding with P800-P1000.
Apply the metallic base coat.
Substrates:
Sanded factory coating.
Metallic or non-metallic base coat.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Mixing: Clearcoat: hardener = 2:1
Pot life: 1.5 hours at 20°C.
Thinning: Vikron acrylic thinner.
Application Viscosity: 15-16 seconds at 20°C using a B3-4 (DIN Cup 4).
Application Equipment:
Compliant spray gun:
Nozzle size: 1.4 - 1.6 mm
Working pressure: 3.0 - 4.0 atm
HVLP spray gun:
Nozzle size: 1.3 - 1.7 mm
Working pressure: 2.0 atm
Flash-off Time: 10 minutes at 20°C.
Coating Thickness: 35-45 microns / 2 layers
Number of Layers: 2-2.5
Drying:
At 20°C — 12 hours
At 60°C — 60 minutes
Equipment Cleaning:
Metallic thinner
Solvent 646/647
Shelf Life: 24 months.

A two-component acrylic clearcoat.

Products:
2K MS acrylic clearcoat
2+1 2+1 MS hardener
Vikron acrylic thinner
Substrates:
Sanded factory coating.
Metallic or non-metallic base coat.
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P240-P320.
Prime the surface that has been sanded down to the metal using WASH PRIMER VL-02 anticorrosion primer.
Apply 2K acrylic primer (3+1, 4+1, or 5+1), followed by dry sanding with P320-P400 or wet sanding with P800-P1000.
Apply the metallic base coat.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Mixing: Clearcoat: hardener = 2:1
Pot life: 1.5 hours at 20°C.
Application Equipment:
Compliant spray gun:
Nozzle size: 1.4 - 1.6 mm
Working pressure: 3.0 - 4.0 atm
HVLP spray gun:
Nozzle size: 1.3 - 1.7 mm
Working pressure: 2.0 atm
Flash-off Time: 10 minutes.
Coating Thickness: 35-45 microns / 2 layers
Number of Layers: 2.5-3
Drying:
At 20°C — 12 hours
At 60°C — 60 minutes
At 80°C — 30 minutes
Equipment Cleaning:
Metallic thinner
Solvent 646/647
Shelf Life: 24 months.

A clear acrylic lacquer with a high solids content, designed for automotive body repair. This lacquer provides excellent coverage, allowing complete painting without overspray areas.

Application Recommendations: Use "VIKRON" thinner (5-10%). Apply the lacquer in 1.5 to 2 layers with a flash-off time of 5-10 minutes at 20°C. The dry film thickness should be 45-65 microns, and drying time before assembly is 24 hours at 20°C.
Mixing ratio: Add hardener for HS Gloss 2+1 lacquer (component B) to the lacquer base (component A) in a 2:1 ratio by volume (2:1 by weight).
Pot life: Must be used within 1.5 hours after mixing with the hardener.
Dilution: Vikron acrylic thinner - 10-20%.
Spraying viscosity: 16-18 sec by DIN 4/20°C.
Application: Apply by pneumatic spraying on a previously painted surface with base coat in 1.5 to 2 layers, allowing a flash-off time between coats and before drying of 5-10 minutes. Flash-off time between coats: 5-10 minutes.
Drying time before assembly: 45 minutes at 60°C, 24 hours at 20°C.
Composition: Solution of acrylic copolymer in organic solvents with the addition of special additives.
Shelf life: 24 months.

Designed for thinning varnishes, paints, enamels, and mastics. To be used according to the instructions provided with the manufacturer's paint and coating materials.
Soluble Materials:

• Paints
• Varnishes
• Enamels
• Adhesives
• Mastics for rubber and leather products.

Also used for degreasing surfaces and refueling blowtorches.

Purpose: A universal hardener designed for curing 2+1 HS and MS acrylic clearcoats. Application: The hardener is added to 2+1 HS and MS acrylic clearcoats just before use, in the amount specified on the label of the paint or coating material.
Composition: Solution of polyisocyanate in organic solvents.

A universal hardener designed for 2K acrylic enamel 4+1 and 2K acrylic primer 5+1 HS.

Products: Universal hardener
Substrates: The Universal Hardener is added just before application in the amount specified on the label of the paint or coating material.
Composition: Polyisocyanate, solvents.

To be used according to the instructions provided with the manufacturer's paint and coating materials.
Soluble Materials:

• Paints
• Varnishes
• Enamels
• Adhesives
• Mastics
• Fillers
• Primers

Designed for thinning metallic enamels. Add directly before using the enamel.
Composition: A mixture of organic liquids.
Shelf Life: 24 months.

A two-component acrylic clearcoat.

Products:
2K acrylic clearcoat 2+1 MS
Hardener for 2+1 MS clearcoat
Vikron acrylic thinner
Substrates:
Sanded factory coating
Metallic or non-metallic base coat
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P240-P320.
Prime the surface that has been sanded down to the metal using WASH PRIMER VL-02 anticorrosion primer.
Apply 2K acrylic primer (3+1, 4+1, or 5+1), followed by dry sanding with P320-P400 or wet sanding with P800-P1000.
Apply the metallic base coat.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Mixing: Clearcoat: hardener = 2:1
Pot life: 1.5 hours at 20°C.
Application Equipment:
Compliant spray gun:
Nozzle size: 1.4 - 1.6 mm
Working pressure: 3.0 - 4.0 atm
HVLP spray gun:
Nozzle size: 1.3 - 1.7 mm
Working pressure: 2.0 atm
Flash-off Time: 10 minutes.
Coating Thickness: 35-45 microns / 2 layers
Number of Layers: 2.5-3
Drying:
At 20°C — 12 hours
At 60°C — 60 minutes
At 80°C — 30 minutes
Equipment Cleaning:
Metallic thinner
Solvent 646/647
Shelf Life: 24 months.

A two-component system designed for automotive body repair painting.
Products:
Enamel AK-1305
Hardener 1305
Vikron acrylic thinner
Substrates:
Sanded factory coating
Primed or filled surfaces
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P240-P320.
Prime the surface that has been sanded down to the metal using WASH PRIMER VL-02 anticorrosion primer.
Apply 2K acrylic primer (3+1, 4+1, or 5+1), followed by dry sanding with P320-P400 or wet sanding with P800-P1000.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Mixing: Enamel: hardener = 2:1
Pot life: 4 hours at +20°C
Thinning: Vikron thinner — 10-20%
Application Viscosity: 18-20 seconds at +20°C using B3-4 (DIN Cup 4).
Application Equipment:
Compliant spray gun:
Nozzle size: 1.4 - 1.6 mm
Working pressure: 2.0 - 4.0 atm
HVLP spray gun:
Nozzle size: 1.3 - 1.7 mm
Working pressure: 2 atm
Drying:
At 20°C — 16 hours
At 60°C — 45 minutes
Flash-off Time: 10 minutes.
Packaging: 0.8 L
Shelf Life: 24 months.

Designed for automotive body repair painting:
Used as the first layer in two-layer coating systems (base + clearcoat).
Applied on pre-primed and filled surfaces.
After applying this layer, it is recommended to cover it with 2+1 MS or HS clearcoat.
Products: Metallic Basecoat
Substrates:
Sanded factory coating
For lacquer coatings with up to 1 year of service, "Anti-silicone" can be used instead of sanding. Primed and filled surfaces
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P280-P320.
Prime the surface with an anticorrosion primer.
Apply leveling primers and sand the surface.
Pot life: 1.5 hours at 20°C
Thinning:
Metallic thinner, up to 30% of the enamel mass.
Application Viscosity:
15-17 seconds at 20°C using B3-4 (DIN Cup 4).
Coating Thickness: 15-20 microns / 2 layers
Number of Layers: 1.5-2
Equipment Cleaning: Solvent 646/647
Shelf Life: 24 months.

Designed for automotive repair painting.

Products:
Enamel AK-1301
Universal acrylic hardener (1301)
Acrylic universal thinner (1301) / slow thinner (1301-M), or their mixture
Substrates:
Sanded factory coating (for enamel coatings with up to 1 year of service life, instead of sanding, "Anti-silicone" can be used)
Primed or filled surfaces
Surface Preparation:
Degrease the metal surface with white spirit.
Repair the surface using polyester filler and perform dry sanding with P280-P320.
Prime the surface with phosphating primer WASH PRIMER VL-02.
Apply leveling primers FILLER 6+1, FILLER 3+1, or FILLER HS.
Perform dry sanding with P320-P400 or wet sanding with P800-P1000.
Application Conditions:
Optimal temperature: +20°C
Minimum temperature: +15°C
Relative humidity: no more than 75%
Mixing:
Enamel: hardener: thinner = 4:1:1.5 (by weight)
Enamel: hardener: thinner = 4:1:1.6 (by volume)
Pot life: 8 hours at +20°C
Drying:
At (20 ± 2)°C — 16 hours
At (60 ± 2)°C — 45 minutes
At (80 ± 2)°C — 30 minutes
Shelf Life: 24 months.